EIGA/PREP Spherical Titanium Alloy Ti 6Al 4V Powder Low Oxygen 3D Printing TC4 Powder
The company uses electrode induction melting atomization (EIGA) powder production methods to produce spherical powders of titanium alloys such as TC4 (Ti-6A1-4V), TA15, TC11, TC18, TINI, TIAL, and titanium based composite materials. These powders have the characteristics of low impurity content, good fluidity, high batch stability, and excellent matching, and can be matched with various powder equipment on the market.
Particle size: 15-53um, 15-45um, 53-150um customized
Product Appearance: Grey spherical powder;
Product features: high purity, complete specifications, controllable particle size, easy sintering, good formability, stable quality Particle size range: Specific production can be carried out according to customer requirements;
Product specifications
典型产品
Typical Product |
TC4(Ti-6Al-4V) |
规 格
Specifications |
0-25 |
0-45 |
15-53 |
53-150 |
15-53 |
53-150 |
粒度分布/μm
Particle Sizo
Distrnibution/μm |
D10 |
7-12 |
12-17 |
18-23 |
62-67 |
20-30 |
55-65 |
| D50 |
10-15 |
27-32 |
32-37 |
82-87 |
35-40 |
95-110 |
| D90 |
18-23 |
45-50 |
55-60 |
130-140 |
50-55 |
140-155 |
球形度
Sphericity |
≥94% |
≥93% |
≥93% |
≥93% |
≥95% |
≥95% |
| 霍尔流速/(s/50g) Flowability/(s/50g) |
|
|
≤40 |
≤35 |
≤30 |
≤25 |
松装密度/(g/cm²)
Apparent Densityi(g/c㎡) |
|
|
2.3-2.5 |
2.3-2.5 |
2.5-2.7 |
2.5-2.7 |
振实密度/(g/cm³)
Tap Densityll(g/cm¹) |
2.70-2.90 |
2.80-2.90 |
2.70-2.90 |
|
|
|
氧含量/(ppm)
Oxygen Content/(ppm) |
<1000ppm (600-1600ppm Available) |
制备工艺
Peparation Methog |
EIGA |
PREP |
化学成分(wt.%)
ChemicalComponent |
Al:5.5~6.75;V:3.5~4.5;Fe≤0.3;C≤0.08;N≤0.05;H≤0.015;Ti:Bal |
技术标准
Technology Standard |
AMS4998,AMS4930,AMS4928,ASTM B348,ASTM F136
ASTM F2924,ASTM F3001,GBT 3620,GBT13810,Gr.5,Gr.23 |
Product Quality Report